Alkaline activated cements obtained from ferrous and non-ferrous slags. Electric arc furnace slag, ladle furnace slag, copper slag and silico-manganese slag

Abstract

Ferrous slag: electric arc furnace slag (EAFS) and ladle furnace slag (LFS); and non-ferrous slag: copper slag (CS) and silicon-manganese slag (SiMnS) have been used as precursors for alkali activated cements (AACs). The objective of the study was to evaluate the effect of the silica modulus (Ms = SiO2/K2O) (0.5–1.8) of the potassium silicate/potassium hydroxide solution on the microstructure and technological properties of AACs using individual slags. The results obtained indicate that under the activation conditions used, CS and EAFS are more reactive slags, giving rise to AACs with optimum flexural and compressive strengths of 7.5 and 51.5 MPa and 5.7 and 30.5 MPa for a Ms = 1.4, respectively. While the SiMnS and LFS are less reactive resulting in AACs with flexural and compressive strengths of 3.2 and 11.6 MPa at Ms = 1.4 for SiMnS and 1.1 MPa and 4.6 MPa at Ms = 0.9 for LFS. In all AACs, the development of the alkaline activation reaction is confirmed due to the presence of gel, of different nature and quantity depending on the precursor used. The lower mechanical properties of the AACs using SiMnS and LFS as precursor may also be due to the presence of microcracks. Therefore, this study confirms that ferrous and non-ferrous slags can be used as precursors of AACs, with the type of precursor and the modulus of the activating solution influencing mechanical properties. AACs using CS and EAFS can be used in structural applications, while those using SiMnS and LFS can be used in non-structural applications in civil engineering.